注氦尖晶石的红外光谱研究
A Study of IR Absorption Behavior of Heliumimplanted Spinel
-
摘要: 利用傅立叶变换红外光谱仪对注He尖晶石样品随退火温变化而引起光吸收性能的变化进行了研究。 发现尖晶石样品在626.4 cm-1附近的吸收峰随注入剂量的增加向小波数方向移动， 而在随后退火过程该吸收峰随退火温度的增加而向大波数方向回复。 该吸收峰的回复行为依赖于注入剂量和退火温度。 认为在626.4 cm-1附近吸收峰随注入剂量和退火温度的这种变化与尖晶石中He的俘获以及释放有关。 The infrared absorption behavior of heliumimplanted spinel with annealing temperature was studied by Fourier transformed infrared (FTIR) spectroscopy. It was found that the absorbance peak at 626.4 cm-1 shifted to smaller wave numbers with the increase of implantation fluence, while on subsequent annealing the absorbance peak shifted back to larger wave numbers with the increase of annealing temperature. The shift of the peak at 626.4 cm-1 with Heimplantation/annealing is considered to be related with the trapping and release of helium atoms in lattice sites in the spinel crystal.Abstract: The infrared absorption behavior of heliumimplanted spinel with annealing temperature was studied by Fourier transformed infrared (FTIR) spectroscopy. It was found that the absorbance peak at 626.4 cm-1 shifted to smaller wave numbers with the increase of implantation fluence, while on subsequent annealing the absorbance peak shifted back to larger wave numbers with the increase of annealing temperature. The shift of the peak at 626.4 cm-1 with Heimplantation/annealing is considered to be related with the trapping and release of helium atoms in lattice sites in the spinel crystal.
下载: