铅离子辐照注碳4H—SiC的红外光谱特性研究
FTIR Characterization of C-ion Implanted and Pb-ion Irradiated 4H-SiC
-
摘要: 主要研究了铅离子辐照注碳4H—SiC样品在3个不同退火温度下傅立叶变换红外光谱的变化。从红外谱的变化可以知道铅辐照注碳4H-SiC样品在一定深度内出现了非晶层，波数在960—1450cm^-1范围内出现了干涉带，干涉带强度随着退火温度的升高而 变弱。1373K退火后样品的卢瑟福背散射分析结果显示，一定深度内硅原子的背散射产额明显减少。4H-SiC specimens were implanted with C-ions and then irradiated with Pb-ions, and subsequently annealed at three different temperatures. The samples were investigated by using Fourier transformation infrared spectrum（FTIR） and Rutherford backward scattering（RBS）. The obtained FTIR spectra showed that there is a buried amorphous layer close to the ion-incident surface and there are several interference fringes in the range from 960 to 1 450 cm ^-1. The intensity of fringes decreases with the increase of annealing temperature. The obtained RBS spectra showed that the yield of Si atoms in 4H-SiC crystal decreases in a well-defined depth region after annealing at 1 373 K.Abstract: 4H-SiC specimens were implanted with C-ions and then irradiated with Pb-ions, and subsequently annealed at three different temperatures. The samples were investigated by using Fourier transformation infrared spectrum（FTIR） and Rutherford backward scattering（RBS）. The obtained FTIR spectra showed that there is a buried amorphous layer close to the ion-incident surface and there are several interference fringes in the range from 960 to 1 450 cm ^-1. The intensity of fringes decreases with the increase of annealing temperature. The obtained RBS spectra showed that the yield of Si atoms in 4H-SiC crystal decreases in a well-defined depth region after annealing at 1 373 K.
下载: